Common Problems and Repair Methods of Cement Rotary Kiln

Rotary kiln is the heart of the cement plant, its main feature is the body weight, high working temperature, thin cylinder steel, easy deformation, with a series of instruments, require a higher level of operation.

Rotary kiln is the heart of the cement plant, its main feature is the body weight, high working temperature, thin cylinder steel, easy deformation, with a series of instruments, require a higher level of operation. Therefore, often due to equipment failure oroperational errors, and cause a variety of accidents. Rotary kiln due to anaccident and stop the kiln, in general, the economic losses are larger, such asa φ3.5 × 145M wet rotary kiln, shut down for an hour, it is necessary to reducethe production of clinker about 25T, the direct economic loss of tens ofthousands of yuan. Therefore, we should try our best to avoid all kinds of accidents or failures so as to reduce the frequency and time of stopping the kiln, which is of great significance to stabilizing the thermal system of thekiln, increasing the output and quality of clinker, reducing the labor intensityof maintenance and increasing the economic benefits. Below I work in the cementplant for many years on the φ3.5 × 145M rotary kiln common accident and failureto analyze - under.

1. Rotary kiln "red kiln"

In the process of raw material burningclinker, the temperature of the airflow in the kiln reaches more than 1600℃, sometimesup to 1800 ℃, the temperature of the material reaches 1450 DEG C, the surfacetemperature of the firing belt barrel is 200℃ to 300℃, Therefractory bricks and the hanging kiln skin play a protective role of thecylinder so that the cylinder is not burned by the high temperature and preventor reduce the temperature in the kiln.

2. Burned Kiln tube body chain

Wet rotary kiln biggest drawback is the lowutilization rate of heat, the general exhaust with 20-30% of the heat, soequipped with a chain at the end of the kiln, so that the initial slurry watervaporization, the exhaust heat away to 10- 6%. However, in the productionprocess, due to improper operation and other reasons, there will be burningchain melting or sintering into a group of major accidents. Such accidentsusually occur in the kiln overhaul to stop burning after the firing stage.Therefore, the operator to strengthen kiln see fire operation, strictimplementation of operating procedures, stop the material must ensure thatsufficient water to join the kiln tail.

3. Kiln cylinder cracks

Cylinder is the main kiln, which usesdifferent thickness of steel rolled into sections after the festival weldedtogether, the general design of the useful life of 30 years, but due tomanufacturing, installation and improper use, and improper maintenance methodsand other reasons, the tube body steel often cracks early, and even cracking causedaccidents.