Factors Influencing Calcination Quality of Rotary Kiln

Rotary kiln rotate while calcine the materials, which ensure that the material is more uniform calcination. The quality of calcination affected by raw materials and block degrees, fuel and other factors.

Rotary kiln rotatewhile calcine the materials, which ensure that the material is more uniform calcination.The quality of calcination affected by raw materials and block degrees, fuel andother factors.

1. Operation. Reasonablydetermine the operating parameters of the kiln (feed volume, speed, flametemperature and length, etc.), can be calcined out the qualified clinker.Operation fluctuation will lead to over-burning or undercooling. Especially calcinehigh temperature raw materials, when the kiln temperature is low, it cannotguarantee to achieve quality requirements.

2. The rawmaterial block degrees. Into the kiln raw materials require uniform blockdegree, block degree is too large, not easy to burn through, block degree istoo small, easy to over burn. Materials in the kiln during the campaign, coarseand fine aggregates produce segregation phenomenon. Fine aggregates are sandwichedin the middle layer, and coarse aggregates roll in the material layer surface.Therefore, coarse aggregates heat better, higher calcination temperature; andthe fine aggregates of the center have opposite condition.

3. Theclassification of raw materials. According to the physical and chemicalproperties of raw materials graded calcination, is conduciveto master the regularity of its calcination and stabilize the kiln thermalsystem. For example, high bauxite Al2O3 content fluctuation range is big,sintering temperature vary with different grades and different requirements,mixed grade material into the kiln will cause the burning of high gradematerial less burn, low grade material over burn, seriously affect the qualityof calcination.

4. Screening rawmaterials before into the kiln. Less than 5mm of the material due to sandwichedimpurities, often have poor quality, which easily fuse into large and smallclumps, not only pollution clinker, but also is difficult to elect; and easy toproduce knot ring kiln, resulting in thermal System damage, affecting thequality of kiln calcination, it must be screened.

5. Fuel. Using coalas fuel, part of the ash settles in the kiln, an increase of the material low meltingcompounds. Therefore, the more calcination process ring, the more is notconducive to the thermal stability of the kiln system, resulting in calcinationquality fluctuations.